MAK 556	FAILURE ANALYSIS OF COMPOSITE MATERIALS	3 + 0	1st Semester	7,5

COURSE DESCRIPTION

Course Level	Master's Degree
Course Type	Elective
Course Objective	To have information about the failure status of composite materials.
Course Content	Damages during the manufacture of composites, Analysis and Causes Damage, Procedure for failure analysis, Damages under tensile loading , Damages under compressive loading, Damages of Axial fiber composites Damages mode of fiber composites, Notch effect of composite materials Temperature effect of compozite materials, Humidty effect of composites, Sem microscopy and interpretation of the results of the damaged composites.,Failure mechanism of short fiber composites ,Failure mechanism of multidirectional composites.
Prerequisites	No the prerequisite of lesson.
Corequisite	No the corequisite of lesson.

COURSE LEARNING OUTCOMES

1	To be inform about; Damage in composites manufacturing • Damage Analysis • Causes • Damages under load • Notch effect the materials • The results and interpretation under SEM • Environmental conditions influence the material • Damage to the effects of fiber orientation

COURSE'S CONTRIBUTION TO PROGRAM

	PO 01	PO 02	PO 03	PO 04	PO 05	PO 06	PO 07	PO 08	PO 09	PO 10	PO 11	PO 12	PO 13	PO 14
LO 001	5	5	5	5	5	5	4	4	5	5	5	5	3	4
Sub Total	5	5	5	5	5	5	4	4	5	5	5	5	3	4
Contribution	5	5	5	5	5	5	4	4	5	5	5	5	3	4

ECTS ALLOCATED BASED ON STUDENT WORKLOAD BY THE COURSE DESCRIPTION

Activities	Quantity	Duration (Hour)	Total Work Load (Hour)
Course Duration (14 weeks/theoric+practical)	14	3	42
Hours for off-the-classroom study (Pre-study, practice)	14	5	70
Mid-terms	1	40	40
Final examination	1	43	43
Total Work Load ECTS Credit of the Course			195 7,5

COURSE DETAILS

Select Year

	Course Term	No	Instructors
Details	2013-2014 Fall	1	NUMAN BEHLÜL BEKTAŞ
Details	2012-2013 Spring	1	DURMUŞ TÜRKMEN

Course Details

Course Code	Course Title	L+P Hour	Course Code	Language Of Instruction	Course Semester	Mode of Delivery
MAK 556	FAILURE ANALYSIS OF COMPOSITE MATERIALS	3 + 0	1	Turkish	2013-2014 Fall	Face to Face

Course Coordinator	E-Mail	Phone Number	Course Location	Attendance
			MUH A02140	%70

Goals		To have information about the failure status of composite materials.
Content		Damages during the manufacture of composites, Analysis and Causes Damage, Procedure for failure analysis, Damages under tensile loading , Damages under compressive loading, Damages of Axial fiber composites Damages mode of fiber composites, Notch effect of composite materials Temperature effect of compozite materials, Humidty effect of composites, Sem microscopy and interpretation of the results of the damaged composites.,Failure mechanism of short fiber composites ,Failure mechanism of multidirectional composites.

Topics

Weeks	Topics
1	Damages during the manufacture of composites,
2	Analysis and Causes Damage, Procedure for failure analysis,
3	PDamages under tensile loading , Damages under compressive loading
4	Damages mode of fiber composites,
5	Damages of Axial fiber composites
6	Damages mode of fiber composites
7	Notch effect of composite materials
8	Midterm Exam
9	Temperature effect of compozite materials,
10	Humidty effect of composites,
11	Sem microscopy and interpretation of the results of the damaged composites.,
12	Sem microscopy and interpretation of the results of the damaged composites.,
13	Failure mechanism of short fiber composites
14	Failure mechanism of multidirectional composites.

Materials

Materials are not specified.

Resources

Resources	Resources Language
Failure Analysis of Industrial Composite Materials, McCraw-Hill	English

Course Assessment

Assesment Methods	Percentage (%)	Assesment Methods Title
Final Exam	50	Final Exam
Midterm Exam	50	Midterm Exam

L+P: Lecture and Practice
PQ: Program Learning Outcomes
LO: Course Learning Outcomes

Prospective Student